Nanjing Union Silicon Chemical Co., Ltd.

                                                Wire & Cable

1,Purpose and Significance of sliane in Wire & Cable

There are three methods in crosslinking polyolefin:by hyperoxide,by irradiation and by silane.Hyoeroxide method has the deficiency of complicated technology demand,untimely crosslinking and difficulty of controlling.Irradiation method is limited by thickness.In opposite,cross-linking through silane has the advantage of simple equipment,simple craft and easy promotion,etc.Due to these advantages,many polyolefin products which crosslinked by silane have realized industrialisation production.What’s more,the stability,solvent resistance and mechanical property of the polyolefin which has been grafting crosslinked by silane also increased a lot which extend the application of polyvinyl.

 2.Silane coupling agent and their reaction theories.

Silane coupling agent is this kind of materials which are usually have two different groups on themselves’ ends. One end’s groups have the chemical action or physics action with the surface of reinforcement, while the other end’s groups can react with base materials, so that well bond the reinforcement with substrate to get the good bonding between interfaces and improve many respects of functions and effectively resist water.

Organicfunctional silane is a kind of surface treating agent with many different and effective kinds and it’s normal chemical structure is RnSiX4-n.

There are four steps to treat filler in Wire & Cable with Organic functional Silane coupling agent:

a.      First, there are three unreliable X groups in atom Si to hydrolyze

b.     Second, the silane coupling agent condensate Oligomers

c.      Third, those oligomers formed hydrogen bond with the “–OH” group of the filler surface.

d.     Last, In the process of drying and curing, silane creates covalent bonds with filler surface.

3.Main silane used in Wire & Cable.

1.Triethoxyvinylsilane                      =USI-402     

2.Vinyltrimethoxysilane                    =USI-401

3.Vinyl tris(2-methoxyethoxy) silane        =USI-412  

4.Different requirement of silane in Wire & Cable.

1.Triethoxyvinylsilane has the fastest speed of hydrolysis which is better for producing warm water silane crosslinked polyethylene.

2.Vinyltrimethoxysilane’s hydrolyzing speed is slower comparatively,which can be used in producing crosslinkable polyolefin.

3.Vinyl tris(2methoxyethoxy) silane has the highest boiling point which is suitable for high temperature processing environment.